The influence of deposition temperature on vanadium dioxide thin films microstructure and physical properties

Authors

  • Velaphi Msomi Cape Peninsula University of Technology
  • Oaisin Nemraoui University of Zululand

Keywords:

deposition temperature, microstructure, thermochromism, thin films, vanadium dioxide

Abstract

Vanadium dioxide thin films were successfully prepared on soda lime glass substrates using the optimised conditions for r.f-inverted cylindrical magnetron sputtering. The optimised deposition parameters were fixed and then a systematic study of the effect of deposition temperature, ranging from 450 °C to 550 °C, on the microstructure of thermochromic thin films was carried out. The deposited films were found to be well crystallised, showing strong texture corresponding to the (011) plane, indicating the presence of vanadium dioxide.

Metrics

Metrics Loading ...

Downloads

Published

2010-11-18

How to Cite

Msomi, V., & Nemraoui, O. (2010). The influence of deposition temperature on vanadium dioxide thin films microstructure and physical properties. South African Journal of Science, 106(11/12), 4 pages. Retrieved from https://sajs.co.za/article/view/10102

Issue

Vol. 106 No. 11/12 (2010)

Section

Research Letters

License

Creative Commons License
All articles are published under a Creative Commons Attribution 4.0 International Licence

Copyright is retained by the authors. Readers are welcome to reproduce, share and adapt the content without permission provided the source is attributed.

Disclaimer: The publisher and editors accept no responsibility for statements made by the authors

Views
  • Abstract 76
  • PDF (341 KB) 63
  • HTML 58
  • XML 38
  • Eqn 1 0
  • Eqn 2 0
  • Eqn 3 0
  • Figure 1 0
  • Figure 2 0
  • Figure 3 0
  • Figure 4 0
  • Figure 5 0
  • Figure 6 0
  • Table 1 & 2 0